A Preliminary Investigation into the Performance of Artificial High Friction Aggregates Manufactured Using Geopolymer Cement-Based Mortars

Despite local and national road authorities striving to provide motorists with a durable and safe infrastructure environment, one in six UK roads are currently classed as being in poor condition. In terms of safety, Department for Transport statistics report high numbers of road incidents; 29,711 killed or seriously injured in 2023, representing little change compared to 2022. As such, reported in this paper is research aimed at developing artificial geopolymer cement mortar-based aggregate as a cost/environmentally attractive alternative to calcined bauxite for high friction surfacing applications. Work was undertaken in two distinct phases. In the first, the performance of alkali silicate-based geopolymers comprising a range of industrial wastes as binder materials was assessed using modified versions of standardized polished stone value and micro-Deval tests. In phase two, selected mixes were assessed for resistance to simulated wear by exposing test specimens to 20,000-wheel passes on an accelerated road test machine. Performance was further investigated using a dynamic friction test method developed by the Indiana Department of Transportation. Despite commercially sourced calcined bauxite aggregates exhibiting the highest performance levels, the findings from this preliminary research were generally positive, with acceptable levels of performance noted for manufactured geopolymer-based aggregates. For instance, in accordance with recommended levels of performance prescribed in BBA/HAPPAS standards, this included attainment of polished stone values higher than 65 and, following accelerated road testing, average texture depths greater than 1.1 mm. It is recognized that further research is needed to investigate geopolymer binder systems and blends of aggregate types, as well as artificial aggregate manufacturing procedures.